Engineered metals
for precision industries

www.robertlaminage.com

MSDS (pdf) Quote request

Al 1050 (99.5)
ALUMINIUM

Chemical composition

Cu0.05 max

Zn0.07 max

Fe0.4 max

Mn0.05 max

Si0.25 max

Al99.5 min

Mg0.05 max

Ti0.05 max

Other0.03 max

*Unified Numbering System (USA)

Physical properties		Units
Density (20°C)	2,71	Kg/dm³
Melting point	640-660	°C
Longitudinal elasticity modulus	69	GPa
Thermal conductivity		W/m·K
Electrical conductivity	>34	m/Ω·mm²
Electrical resistivity	<0.029	µΩ·m
Linear expansion Coefficient	23,6	10⁻⁶·K⁻¹
IACS (International Annealed Copper Standard)	59	%
Poisson's ratio	0,33

1 poor | 2 average | 3 good | 4 very good | - no info

Heat Treatment / Hardening
Annealing temperature	350-450	°C
Temperature for stress relief treatment	150	°C
Hardening temperature		°C
Hardening treatment time		hour(s)

Al 1050 (99.5)
Possible hardness range	30 - 45	HV
Possible Rm range	-	MPa

Grade	Hardness (HV: Vickers) min - max	Rm (MPa) min - max	Rp 0.2 (MPa) min - max	Elongation (%) where L0 = 100mm min - max
O, H111	30*	65 - 95	≥ 20	≥ 32
H12		85 - 125	≥ 65	≥ 9
H14		100 - 140	≥ 80	≥ 6
H16		120 - 160	≥ 100	≥ 5
H18	45*	≥ 140	≥ 125	≥ 4

Do not hesitate to ask us for your specific grades and parameters. We can make productions according to your needs.