AlCuMgSi
AVIONAL 102 - EN AW2017A

Chemical composition

Cu3.5-4.5

Zn0.25 max

Fe0.7 max

Mn0.40-1.00

Si0.20-0.80

AlBAL

Mg0.40-1.00

TiTi+Zr 0.25

Cr0.1 max

Other0.15 max

*Unified Numbering System (USA)

Physical properties		Units
Density (20°C)	2,78	Kg/dm³
Melting point	510-650	°C
Longitudinal elasticity modulus	72	GPa
Thermal conductivity		W/m·K
Electrical conductivity	>27	m/Ω·mm²
Electrical resistivity	<0.037	µΩ·m
Linear expansion Coefficient	23,6	10⁻⁶·K⁻¹
IACS (International Annealed Copper Standard)	47	%
Poisson's ratio	0,33

1 poor | 2 average | 3 good | 4 very good | - no info

Heat Treatment / Hardening
Annealing temperature	350-500	°C
Temperature for stress relief treatment		°C
Hardening temperature	150-200	°C
Hardening treatment time	6 - 16	hour(s)

Mise en solution proche de la temp de fusion + Vieillissement 150-200°C

AlCuMgSi
Possible hardness range	55 - 180	HV
Possible Rm range	240 - 330	MPa

Grade	Condition	Hardness (HV: Vickers) min - max	Rm (MPa) min - max	Rp 0.2 (MPa) min - max	Elongation (%) where L0 = 100mm min - max
O	ISO 6361-2(2011)		≤ 225	≤ 145	≥ 12
T4	ISO 6361-2(2011)		≥ 390	≥ 245	≥ 14
ROBT9	RLSA	160-180